01
Monel K-500 Rough-Turned Forged Bar
Turned heavy stock leaving a machining allowance on the diameter.
Request Availability →Monel K-500 Forged Bar
Monel K-500 forged bar to ASTM B865 itself for heavy pump casings, valve bodies and marine shafting.
Aging Sets the Strength
Aluminium and titanium in this Monel K-500 forged bar precipitate during the aging cycle, so yield lands near three times the Monel 400 figure.
Non-Magnetic by Nature
Moreover, permeability in this Monel K-500 forged bar stays near unity, which keeps survey and instrument parts reading clean.
Sour Service Under a Cap
Furthermore, we hold this Monel K-500 forged bar to the 35 HRC ceiling that NACE MR0175 sets for H2S-bearing duty.
PRODUCT OVERVIEW
About Monel K-500 Forged Bar
Monel K-500 forged bar arrives in UNS N05500, the age-hardenable nickel-copper alloy that carries aluminium and titanium in its balance. Seawater, brine and de-aerated reducing acids meet this Monel K-500 forged bar at roughly triple the Monel 400 yield floor.
We supply Monel K-500 forged bar to ASTM B865 and ASME SB865 in solution-annealed, age-hardened and cold-drawn conditions. Your order for this Monel K-500 forged bar carries heat-number records and EN 10204 3.1 paperwork for goods-in checks. Besides, the aging cycle, section and finish on the forged bar are agreed before the heat is booked.
Meanwhile, the chemistry and the design values behind Monel K-500 forged bar sit on our Monel K-500 material page for cross-reference.
PRODUCT FEATURES
Key Features of Monel K-500 Forged Bar
Monel K-500 forged bar arrives in UNS N05500, the age-hardenable nickel-copper alloy that carries aluminium and titanium in its balance. We provide ASTM B865 and ASME SB865 forged bar in forged, rough-turned and age-hardened conditions for marine yards, sour-gas tool shops and chemical plant. Every Monel K-500 forged bar order carries heat-number traceability, EN 10204 3.1 mill test reports and full export documentation.
Monel K-500
Yield Near Triple the 400 Grade
For example, this Monel K-500 forged bar reaches about 100 ksi yield where Monel 400 settles near 25 ksi.
01
Aging Not Cold Work
Specifically, precipitation hardening sets the final properties of this Monel K-500 forged bar, so drawing becomes a pre-treatment.
02
Essentially Non-Magnetic
Besides, permeability in this Monel K-500 forged bar stays near unity, which keeps magnetometers and compasses honest.
03
Hardness to Order
In turn, the aging cycle lands this Monel K-500 forged bar inside the hardness band your purchase order names.
04
Sour-Service Cap
Moreover, we release this Monel K-500 forged bar against the 35 HRC ceiling that NACE MR0175 sets.
05
Wear and Fatigue Life
Hardened surfaces on this Monel K-500 forged bar resist galling and cyclic loading in stems and fasteners.
06
Aged-State SCC Review
However, some media make aged this Monel K-500 forged bar more crack-prone, so we review HF, mercury and sour duty with you.
07
Cryogenic Ductility
Finally, no ductile-to-brittle transition appears, so this Monel K-500 forged bar keeps its toughness down to liquid-hydrogen temperatures.
08
WHY CHOOSE US
Why Choose Monel K-500
Heavy sections make the forging route the first question for Monel K-500 forged bar. Therefore, we agree the reduction plan and the test position on this Monel K-500 forged bar before we price it.
01
Duty Read Before Pricing
We record the load, the medium and the hardness cap your Monel K-500 forged bar will meet before proposing a delivery state.
02
Certificates Tied to the Heat
Specifically, EN 10204 3.1 papers, heat numbers and PMI records follow each Monel K-500 forged bar delivery.
03
Trial Pieces and Container Lots
In addition, this Monel K-500 forged bar moves through one route whether you need a single length or a full container.
04
Terms Stated in Writing
Quotations for this Monel K-500 forged bar name the delivery state, section, finish and document set instead of leaving them open.
MANUFACTURING PROCESS
Reliable Production For Critical Applications
Bar production for Monel K-500 forged bar runs from charge weighing to final packing. Our team logs each stage of this Monel K-500 forged bar route against its heat number.
01
Charge Weighing
Charge weighing comes first, and this Monel K-500 forged bar starts from refined nickel and cathode copper.
02
Melting and Refining
First, the charge for this Monel K-500 forged bar melts and refines under controlled practice.
03
Ingot Casting
Next, this Monel K-500 forged bar casts into ingots under controlled solidification.
04
Hot Reduction
Then, forging and rolling reduce the ingot to this Monel K-500 forged bar section.
05
Solution Treatment
After that, we hold this Monel K-500 forged bar near 980 °C and quench it rapidly to keep aluminium and titanium in solution.
06
Precipitation Aging
Subsequently, a controlled cycle at 530 to 595 °C precipitates the hardening phase inside this Monel K-500 forged bar.
07
Cold Finishing
We then draw, turn or grind this Monel K-500 forged bar to the ordered size and finish.
08
Testing and Release
Finally, chemistry, hardness, tensile and dimensional checks clear this Monel K-500 forged bar for dispatch.
Manufacturing Facility
MANUFACTURING CAPABILITY
Advanced Production For Nickel Alloy Products
Stock lengths and made-to-order lots of Monel K-500 forged bar leave on one schedule. Moreover, we confirm section and condition of this Monel K-500 forged bar before release. Besides, this Monel K-500 forged bar sits inside our Monel K-500 bar and rod program.
20,000+ m²
Factory Area
Specifically, melting, forging, aging and inspection halls serve Monel K-500 forged bar under one roof.
50+
Production Machines
Equipment covering hot working, solution treatment and cold finishing for this Monel K-500 forged bar.
600 Tons
Monthly Capacity
Monel K-500 forged bar output across stock and made-to-order sizes.
30+
Technical Engineers
Metallurgists who set the aging cycle and document scope of this Monel K-500 forged bar against your duty.
30+ Countries
Export Reach
In addition, documented logistics carry this Monel K-500 forged bar worldwide.
QUALITY ASSURANCE
Strict Quality Control From Production To Delivery
No Monel K-500 forged bar leaves the yard before its heat has cleared our ISO 9001 inspection route. In addition, we check this Monel K-500 forged bar against the chemistry, hardness, dimensions and surface the order names.
01
Heat Identification
We confirm the grade and heat number of this Monel K-500 forged bar against your purchase order.
02
Hardness Verification
Specifically, aged stock of this Monel K-500 forged bar goes against the ordered band, and NACE orders target 35 HRC max.
03
Dimensional Verification
In addition, the size, length and straightness of this Monel K-500 forged bar go against standard and drawing tolerances.
04
Certificate Assembly
Every consignment of this Monel K-500 forged bar carries EN 10204 3.1 documents keyed to the heat number.
PRODUCT FORMS
Available Product Forms
Conditions and variants of Monel K-500 forged bar cover different machining and service needs. In addition, the list below sets out the Monel K-500 Forged Bar variants we quote most often.
02
Monel K-500 Forged Square Bar
Forged squares for blocks and heavy posts.
Request Availability →
03
Monel K-500 Forged Flat Bar
Forged flats for thick plate-like fabrications.
Request Availability →
04
Monel K-500 Forged Block
Blocks cut from forged stock for further machining.
Request Availability →
05
Monel K-500 Forging Stock
Stock sized for downstream forging and ring rolling.
Request Availability →
06
Monel K-500 Custom Forged Section
Forged sections produced to your drawing and heat treatment.
Request Availability →
APPLICATIONS
Engineered For Demanding Industries
Monel K-500 forged bar is chosen where seawater duty and heavy load meet in one component. In addition, the applications below show where this Monel K-500 forged bar serves.
Discuss Your Application →
01
Monel K-500 Heavy Pump Casings
Casing bodies forged for large pumps moving salt water and brine.
02
Monel K-500 Valve Bodies
Body stock for valves in HF, seawater and reducing-acid duty.
03
Monel K-500 Heat-Exchanger Shells
Forged shell and closure stock for marine exchangers.
04
Monel K-500 Propeller Shaft Flanges
Flange blanks machined from heavy forged sections.
05
Monel K-500 Rolled Ring Blanks
Forged stock feeding ring-rolling and seal lines.
06
Monel K-500 Wellhead Bodies
Forged bodies for sour-service wellhead hardware.
07
Monel K-500 Agitator Shafts
Heavy shafts for mixers in acid and brine reactors.
08
Monel K-500 Custom Heavy Sections
Bespoke forged sections for one-off plant projects.
TECHNICAL INFORMATION
Technical Specifications
Detailed technical information including chemical composition, mechanical properties, standards and available dimensions.
Chemical Composition
UNS N05500 carries the same nickel balance as the 400 grade and adds aluminium at 2.30% to 3.15% together with titanium at 0.35% to 0.85%. Consequently, this forged bar draws its strength from a controlled aging cycle rather than from a drawing pass. Besides, the copper window runs from 27.0% to 33.0%.
For the full element-by-element limit set, open the composition breakdown held on the Monel K-500 material page for this forged bar.
Mechanical Properties
The minimum room-temperature values below apply to UNS N05500 bar in the hot-worked, cold-worked and annealed conditions, all in the age-hardened state, per ASTM B865. Consequently, condition and section size govern final acceptance of Monel K-500 forged bar.
| Condition and Section | Tensile Strength, min. | Yield Strength (0.2%), min. | Elongation, min. |
|---|---|---|---|
| Hot-worked and age-hardened, all sizes | ≥140 ksi (965 MPa) | ≥100 ksi (690 MPa) | 20% |
| Cold-worked and age-hardened, rounds 6.4–25.4 mm (1/4–1 in.) | ≥145 ksi (1000 MPa) | ≥110 ksi (760 MPa) | 15% |
| Cold-worked and age-hardened, rounds 25.4–76.2 mm (1–3 in.) | ≥140 ksi (965 MPa) | ≥100 ksi (690 MPa) | 17% |
| Cold-worked and age-hardened, rounds 76.2–101.6 mm (3–4 in.) | ≥135 ksi (930 MPa) | ≥95 ksi (655 MPa) | 20% |
| Annealed and age-hardened, rounds to 25.4 mm (1 in.) | ≥130 ksi (895 MPa) | ≥90 ksi (620 MPa) | 20% |
| Annealed and age-hardened, rounds over 25.4 mm (1 in.) | ≥130 ksi (895 MPa) | ≥85 ksi (585 MPa) | 20% |
- ASTM B865 accepts the unaged condition on hardness alone with a 185 HB ceiling, and rounds over 108 mm relax to a 17% elongation minimum, so the ordered condition and section decide which row applies.
Physical Properties
Published references place this forged bar at a density near 8.44 g/cm³ with a melting range of 1315–1350 °C. Moreover, the Curie temperature sits near −101 °C, so this forged bar stays essentially non-magnetic at ambient temperature.
Meanwhile, the physical properties table on the Monel K-500 material page holds the thermal conductivity, the electrical resistivity and the remaining design values behind this forged bar.
Heat Treatment
Monel K-500 forged bar gains its strength from solution treatment followed by a controlled aging cycle, so the heat treatment is part of the specification rather than an optional step. In addition, we supply this Monel K-500 forged bar in whichever condition your duty calls for.
| Condition | Typical Treatment |
|---|---|
| Solution Annealed | Held near 980 °C and rapidly quenched to hold aluminium and titanium in solution |
| Aged from Annealed Stock | Held at 580–595 °C (1075–1105 °F) for 8 to 10 hours, then air cooled |
| Aged from Spring Temper | Held at 530–540 °C (985–1005 °F) for 4 to 6 hours, then air cooled |
| Stress Relieved | A low-temperature relief that holds straightness without starting the precipitation |
Standards
Heavy sections of this forged bar are quoted to ASTM B865 itself, published by ASTM International, because that scope runs past bar and rod into forgings and forging stock. Moreover, AMS 4676 and DIN 17754 cover the forged bar and ring forms of this forged bar.
| Standard | Product or Application |
|---|---|
| ASTM B865 | Scope runs into forgings and forging stock, UNS N05500 |
| AMS 4676 | Forged bar and ring forms of this grade |
| DIN 17754 | Nickel-copper forging stock, Europe |
Finally, the full standards list on the Monel K-500 material page adds the European designations, the defence documents and the fastener specifications behind this forged bar.
Dimensions
Dimensions of Monel K-500 forged bar follow the manufacturing route, the standard and the order quantity. Therefore, the table below lists typical supply ranges, so please confirm your size in the inquiry.
| Product Form | Typical Supply | Length |
|---|---|---|
| Forged Round Bar | 100–600 mm dia. | Cut to length |
| Forged Square Bar | 100–300 mm | Cut to length |
| Forged Flat Bar | 20–150 mm thick × 50–400 mm wide | Cut to length |
| Rough-Turned Forged Bar | 100–600 mm dia. | Cut to length |
| Age-Hardened Forged Bar | 100–600 mm dia. | Cut to length |
| Forging Stock | 100–500 mm sections | Custom |
| Custom Forged Section | To drawing | Custom |
Available sizes of this Monel K-500 forged bar depend on the manufacturing route, the standard, the material condition and the order quantity. Please confirm your required forged bar size, section and length in the inquiry.
ASTM B865 carries forgings and forging stock inside its own scope for UNS N05500, so no separate forging document is needed for this Monel K-500 forged bar. Moreover, AMS 4676 and DIN 17754 serve aerospace and European projects, and the aging cycle is recorded per heat.
Surface Finishes
Finish decides what the next operation does to this material, whether that is a turning pass, a grinding pass or an aging cycle. Specifically, we fix the finish on this Monel K-500 forged bar before the order is released.
| Surface Condition | Typical Use |
|---|---|
| Hot-Worked | As-rolled or as-forged surface on this forged bar, for parts that will be machined all over. |
| Rough Turned | A turned surface on this forged bar where the finishing cut is left to your shop. |
| Descaled and Ground | Uniform descaled surface on this forged bar for inspection and coating. |
Meanwhile, the surface finishes table on the Monel K-500 material page lists the remaining conditions we quote for this forged bar.
Related forms from the same heat cover Monel K-500 Hex Bar, Monel K-500 Round Bar and Monel K-500 Square Bar when your forged bar order needs them.
TECHNICAL DOCUMENTATION
Download Technical Datasheet
Get detailed information including specifications, standards, dimensions and material properties.
HOW TO START
Start Your Order in 6 Simple Steps
One coordinator carries your Monel K-500 forged bar order from first question to loading. Therefore, most orders for this Monel K-500 forged bar move from quotation to dispatch inside three weeks.
1
Send the Duty Data
Give the size, quantity, standard and the load or medium your Monel K-500 forged bar will see.
2
Fix the Condition
Then we set the delivery state, aging cycle and tolerance for this Monel K-500 forged bar.
3
Review the Offer
Receive pricing for this Monel K-500 forged bar by dimension, quantity and destination port.
4
Approve the Order
Approve the specification, terms and schedule for this Monel K-500 forged bar in writing.
5
Witness Points Agreed
Any third-party inspection or NACE review of this Monel K-500 forged bar is booked before production starts.
6
Dispatch and Documents
Receive this Monel K-500 forged bar with the mill certificate, packing list and shipping papers.
CERTIFICATIONS & QUALITY DOCUMENTATION
Certifications & Quality Documentation
Our production and inspection processes are certified to international standards, and every delivery ships with EN 10204 3.1 mill test certificates.
ISO 9001:2015
Quality Management System
PED 2014/68/EU
Pressure Equipment Directive
ASTM / ASME
Material Standards Compliance
EN 10204 3.1
Mill Test Certificates
FAQ
Frequently Asked Questions
Which standard covers this Monel K-500 forged bar?
ASTM B865 and ASME SB865 govern this Monel K-500 forged bar for UNS N05500 across round, square, hex and rectangular sections.
Does this Monel K-500 forged bar arrive in the aged condition?
Yes. This forged bar ships solution-annealed for machining or fully aged at the ordered hardness band, and NACE orders for this Monel K-500 forged bar target 35 HRC max.
Should this Monel K-500 forged bar be machined before or after aging?
Rough machine this forged bar before aging and finish afterwards, because the section contracts slightly during the cycle.
Is this Monel K-500 forged bar suitable for seawater?
Yes. This forged bar performs well in flowing seawater at aged strength, although static water and silt traps raise the pitting risk on this Monel K-500 forged bar.
How is the price of this Monel K-500 forged bar calculated?
Pricing follows weight for this Monel K-500 forged bar, with the nickel, copper and aluminium quotations fixed on the date you receive the offer.
What is your MOQ for this Monel K-500 forged bar?
A single piece covers many common sizes of this Monel K-500 forged bar.
What are your trade terms for this Monel K-500 forged bar?
FOB covers most orders for this Monel K-500 forged bar, and EXW or CIF terms are available when you ask.
What is the lead time for this Monel K-500 forged bar?
Stock sizes of this Monel K-500 forged bar dispatch in 7 to 15 days, while made-to-order sections and custom aging take longer.
Do you provide EN 10204 3.1 or 3.2 certificates for this Monel K-500 forged bar?
Yes. Every heat of this Monel K-500 forged bar ships with 3.1, and a 3.2 endorsement is booked through the order.
What information should an enquiry for this Monel K-500 forged bar include?
Please send the grade, section, diameter, length, delivery state, finish, quantity and destination so we can quote this Monel K-500 forged bar accurately.
REQUEST FOR QUOTATION
Need A Custom Alloy Solution?
Monel K-500 forged bar runs to ASTM B865 with the test position agreed before melting. Send the section, weight and any drawing so we can quote this Monel K-500 forged bar.
Specifically, we review your Monel K-500 forged bar specification, confirm the aging route and document scope, and return pricing with clear terms. Production then follows the signed specification, and each consignment of this Monel K-500 forged bar ships with the full paperwork set.