Inconel 600 Hot-Rolled Plate
Plate from 4.8 mm thick in annealed or as-rolled condition for vessels and furnace hardware.
View Inconel 600 Hot-Rolled Plate →Inconel 600 Plate and Sheet — ASTM B168 Supply
UNS N06600 hot-rolled and cold-rolled plate, sheet, and strip to B168 for furnace, caustic, and chemical service.
Full B168 Gauge Range
Strip, sheet, and plate from 0.13 mm to 100 mm thick is quoted under one UNS N06600 inquiry.
Condition Options
Gauges ship annealed for forming or as-rolled where the higher minimum strength helps.
Cut-to-Size Supply
Plate and sheet are cut to length and width against your fabrication drawings before shipment.
PRODUCT OVERVIEW
About Inconel 600 Plate and Sheet
Inconel 600 Plate and Sheet are supplied in UNS N06600, a nickel-chromium-iron alloy rolled for oxidation and caustic duty. Meanwhile, chloride stress-corrosion cracking stays out of the picture in furnace and alkaline equipment. Therefore, every gauge is quoted from ASTM B168 under B906 general requirements.
PRODUCT FEATURES
Key Features of Inconel 600 Plate and Sheet
Southerly Alloy supplies UNS N06600 plate, sheet, and strip to ASTM B168 in hot-rolled, cold-rolled, and annealed conditions. Gauges run from 0.13 mm strip to 100 mm plate, cut to length and width against your fabrication drawings. EN 10204 3.1 certificates and heat-level traceability support furnace builders, caustic processors, and chemical equipment review.
Inconel 600
Oxidation Resistance to 1093 °C
Plate and sheet hold their protective oxide scale through repeated furnace cycles.
01
Caustic Service Reliability
NaOH and KOH equipment runs without the stress-corrosion cracking seen in stainless plate.
02
Chloride SCC Resistance
At this nickel level, chloride-ion stress-corrosion cracking rarely enters the design conversation.
03
Hot-Rolled Strength Option
As-rolled plate carries a 585 MPa (85 ksi) tensile minimum for heavier load paths.
04
Wide Gauge Window
Strip from 0.13 mm and plate to 100 mm cover cladding, lining, and fabrication needs together.
05
Formable Annealed Condition
Cold forming and welding proceed without an age-hardening step.
06
Heat-Level Traceability
EN 10204 3.1 certificates tie every flat-product shipment to its melting heat.
07
WHY CHOOSE US
Why Choose Inconel 600
Flat-product orders are coordinated by Southerly Alloy and executed at audited partner plants that melt and roll this grade. Your enquiry reaches the plant responsible for melting, rolling, and finishing the plate. Therefore, gauge, condition, and cutting decisions move in one conversation from inquiry onward.
01
Condition Selection
Annealed or as-rolled delivery is chosen against your forming plan and load path before quotation.
02
Cut-to-Length Capability
Plasma, saw, and shear cutting bring plate to your blank geometry before dispatch.
03
Inspection Scope
Ultrasonic testing, PMI, and third-party inspection are attached to the order as the service requires.
04
Export Delivery
Shipping cartons, Incoterms, and destination documents are arranged by the same coordination team.
MANUFACTURING PROCESS
Reliable Production For Critical Applications
UNS N06600 flat product follows a controlled route from melt to finished plate. Also, the route flexes toward the ordered gauge, standard, and acceptance level.
01
Charge and Melting
Nickel, chromium, and iron charge are melted under vacuum to the UNS N06600 chemistry window.
02
Remelting Where Specified
ESR refining improves ingot cleanliness for nuclear and aerospace-bound heats.
03
Hot Rolling
Slabs are hot rolled to plate and sheet gauge with controlled reduction and finish temperature.
04
Cold Rolling
Strip and thin sheet are cold rolled to gauge with tighter tolerance and improved surface.
05
Annealing
Furnace annealing between 900 and 1050 °C restores the soft condition before descaling.
06
Cutting and Inspection
Material is straightened, cut to size, and tested to the ordered acceptance level.
Manufacturing Facility
MANUFACTURING CAPABILITY
Advanced Production For Nickel Alloy Products
Hot-rolled and cold-rolled Inconel 600 flat product is supplied from 0.13 mm strip through 100 mm plate. Gauge, width, length, condition, and edge finish are confirmed against your purchase requirements before rolling. As a result, the plan quoted at inquiry is the plan that runs.
20,000+ m²
Factory Area
Hot rolling, cold rolling, and finishing share dedicated nickel-alloy workshops.
50+
Production Machines
Rolling, annealing, leveling, and cutting lines operate under one quality system.
600 Tons
Monthly Capacity
Plate, sheet, and strip output across standard and custom gauges.
30+
Technical Engineers
Gauge, condition, and acceptance decisions are settled before the order.
QUALITY ASSURANCE
Strict Quality Control From Production To Delivery
Every flat-product batch passes the ordered acceptance checks before release, covering chemistry, mechanics, gauge, and surface under the ISO 9001 system. Above all, each shipment leaves with an EN 10204 3.1 certificate, and third-party inspection can be added at order stage.
01
Chemical Analysis
Spectrometer results are compared with the UNS N06600 limits on every heat.
02
Mechanical Testing
Tensile, yield, and elongation are confirmed on the ordered condition and gauge.
03
Dimensional and Surface Checks
Thickness, flatness, and edge condition are examined, with UT on request.
04
Documentation
Heat-number traceability supports the EN 10204 3.1 certificate on all deliveries.
PRODUCT FORMS
Available Product Forms
Four flat-product forms cover the UNS N06600 sheet and plate range. Each form follows its own finishing route under ASTM B168.
02
Inconel 600 Cold-Rolled Sheet
Sheet from 0.46 to 6.35 mm with improved surface for forming and lining work.
Request Availability →
03
Inconel 600 Strip and Coil
Coil from 0.13 to 6.35 mm slit to width for roll forming and stamping.
Request Availability →
04
Cut Blanks
Circles, rings, and profile-cut plate produced to customer drawings from any stocked gauge.
Request Availability →
APPLICATIONS
Engineered For Demanding Industries
Flat-product duty here is governed by heat and alkali, while chloride pitting sits lower on the threat list. For that reason, the uses below match oxidation or caustic performance to the temperature each line runs.
Discuss Your Application →
01
Heat-Treatment Trays and Fixtures
Furnace hardware cycling between ambient and operating temperature.
02
Furnace Muffles and Liners
Plate components shielding insulation from oxidation at 800 to 1100 °C.
03
Caustic Evaporator Shells
NaOH and KOH vessels where stainless plate suffers stress-corrosion cracking.
04
Chemical Vessels and Stills
Fatty acid heaters, bubble towers, and reactor internals at temperature.
05
Nuclear Reactor Hardware
Components in high-purity water qualified for reactor service.
06
Flaking Trays
Sodium sulfite and similar crystallizer duty with thermal cycling.
07
Dry Chlorine Equipment
Vessels and ducting for dry halogen service at elevated temperature.
08
Thermal-Cycling Fixtures
Fabricated supports under repeated heat-up and cool-down.
TECHNICAL INFORMATION
Technical Specifications
Detailed technical information including chemical composition, mechanical properties, standards and available dimensions.
Chemical Composition
The chemistry window below is common to the B168 flat-rolled family for UNS N06600. However, the governing purchase specification takes precedence for acceptance.
| Element | Content |
|---|---|
| Nickel (Ni) | 72.0% min. |
| Chromium (Cr) | 14.0–17.0% |
| Iron (Fe) | 6.0–10.0% |
| Carbon (C) | 0.15% max. |
| Manganese (Mn) | 1.00% max. |
| Silicon (Si) | 0.50% max. |
| Sulfur (S) | 0.015% max. |
| Copper (Cu) | 0.50% max. |
Mechanical Properties
Minimum room-temperature values below follow ASTM B168 for the hot-rolled and cold-rolled conditions. Therefore, the applicable condition must be specified for final acceptance.
| Product Form | Standard | Condition | Tensile Strength | Yield Strength, 0.2% Offset | Elongation |
|---|---|---|---|---|---|
| Hot-rolled plate | ASTM B168 | Annealed | ≥550 MPa (80 ksi) | ≥240 MPa (35 ksi) | ≥30% |
| Hot-rolled plate | ASTM B168 | As-rolled | ≥585 MPa (85 ksi) | ≥240 MPa (35 ksi) | ≥30% |
| Sheet and strip | ASTM B168 | Annealed | ≥550 MPa (80 ksi) | ≥240 MPa (35 ksi) | ≥30% |
Aerospace AMS 5540 deliveries carry condition-specific minimums and extra process controls. Confirm the required condition at inquiry so the correct standard is quoted.
Physical Properties
| Property | Value |
|---|---|
| Alloy | Inconel 600 |
| UNS | N06600 |
| Werkstoff | 2.4816 |
| Density | Approx. 8.47 g/cm³ |
| Melting Range | Approx. 1370–1413 °C |
| Elastic Modulus | Approx. 214 GPa |
| Thermal Conductivity | Approx. 14.8 W/m·°C at 20 °C |
| Expansion Coefficient | 13.3 µm/m·°C (20–100 °C) |
| Alloy Type | Nickel-chromium-iron |
Standards
| Standard | Product / Application |
|---|---|
| ASTM B168 / ASME SB168 | Plate, sheet, and strip |
| ASTM B906 | General requirements for nickel alloy flat-rolled product |
| SAE AMS 5540 | Sheet, strip, and plate |
| DIN 17750 | Nickel alloy plate, sheet, and strip, W.Nr. 2.4816 |
| ISO 6208 | Nickel and nickel alloy plate, sheet, and strip |
| UNS N06600 · W.Nr. 2.4816 · NiCr15Fe | Designations |
ASTM publishes the governing documents at ASTM International, and the ASME counterpart applies once the equipment falls under code jurisdiction. Additionally, furnace and caustic designers should confirm service limits against the process data for each project.
Dimensions
| Product Form | Typical Supply Range | Length |
|---|---|---|
| Hot-rolled plate | 4.8–100 mm thick, widths to 2500 mm | Cut to length and width |
| Cold-rolled sheet | 0.46–6.35 mm thick, widths to 1500 mm | Cut to length and width |
| Strip and coil | 0.13–6.35 mm thick, slit to width | Coil or custom lengths |
| Cut blanks | Any stocked gauge | To customer drawing |
Sizes outside the listed windows are quoted against slab and coil availability. Therefore, state thickness, width, length, condition, and edge finish in the inquiry for an accurate route and price.
Surface Finishes
| Surface Condition | Typical Characteristics / Applications |
|---|---|
| Annealed & Pickled | Standard delivered condition for forming and fabrication |
| Bright Annealed | Smooth, scale-free surface for visible and clean service |
| Pickled Only | Acid-descaled surface for general industrial fabrication |
| Mill Finish | As-rolled surface for machining and further processing |
TECHNICAL DOCUMENTATION
Download Technical Datasheet
Get detailed information including specifications, standards, dimensions and material properties.
HOW TO START
Start Your Order in 6 Simple Steps
A typical sheet or plate inquiry reaches shipment in two to four weeks, though heavy plate needs longer. Before price is fixed, the sequence below aligns standard, condition, and cutting scope with your fabrication plan.
1
Send Your Inquiry
List thickness, width, length, quantity, condition, and the equipment the material serves.
2
Select the Standard
Choose B168 for industrial plate and sheet, or AMS 5540 for aerospace gauges.
3
Confirm the Condition
Annealed material suits forming and welding, while as-rolled plate favors strength.
4
Review the Quotation
Price follows the rolling route, cutting scope, testing, documentation, and Incoterm.
5
Production and Inspection
The mill runs rolling, annealing, and testing to the level agreed at quotation.
6
Shipment and Documentation
Your order departs with 3.1 certificates and the full export file.
What Our Clients Say
Feedback from buyers and engineers who source nickel alloy materials from Southerly Alloy.
★★★★★
“The annealed B168 plate for our caustic evaporator shells arrived flat, clean, and cut to our blank list without a single rework.”
★★★★★
“Furnace liner sheet held the gauge across the whole order, and the 3.1 certificates were ready at collection.”
★★★★★
“As-rolled plate for our fixture build was documented heat by heat, so incoming inspection took minutes instead of days.”
CERTIFICATIONS & QUALITY DOCUMENTATION
Certifications & Quality Documentation
Our production and inspection processes are certified to international standards, and every delivery ships with EN 10204 3.1 mill test certificates.
ISO 9001:2015
Quality Management System
PED 2014/68/EU
Pressure Equipment Directive
ASTM / ASME
Material Standards Compliance
EN 10204 3.1
Mill Test Certificates
FAQ
Frequently Asked Questions
Which ASTM standard covers Inconel 600 plate and sheet?
ASTM B168 covers hot-rolled and cold-rolled plate, sheet, and strip, while B906 governs general flat-rolled requirements. ASME SB168 applies under code jurisdiction.
What thickness range is available for Inconel 600 plate?
Supply runs from 0.13 mm strip through 100 mm hot-rolled plate, cut to length and width. Meanwhile, heavier sections are quoted against slab availability.
What is the maximum temperature for Inconel 600 flat product?
Continuous oxidation service runs to about 1093 °C (2000 °F). Nevertheless, the exact design temperature should be confirmed against load and medium for each application.
Can Inconel 600 plate be supplied in the as-rolled condition?
Yes. As-rolled hot-rolled plate carries a 585 MPa (85 ksi) tensile minimum under B168, and it is quoted against your load path and forming plan.
How is Inconel 600 plate priced?
Inconel 600 plate is typically priced by weight (kg) against the ordered gauge, width, and required delivery terms. The applicable Incoterm is stated on every quotation.
What is your MOQ for Inconel 600 sheet?
One piece is accepted for many stocked gauges, so trial fabrication and repair orders carry no premium hurdle.
What are your trade terms for Inconel 600 plate?
FOB serves as the default Incoterm, while EXW, CIF, and DAP quotes follow confirmed destinations.
What is the lead time for Inconel 600 plate?
Mill production for standard gauges runs 7-15 days, and cut-to-size or as-rolled product is quoted against the confirmed production schedule.
Do you provide EN 10204 3.1 or 3.2 certificates?
Yes. Every delivery ships with an EN 10204 3.1 certificate, and 3.2 endorsement through a third party is available on request.
REQUEST FOR QUOTATION
Need A Custom Alloy Solution?
Send the thickness, width, length, standard, and quantity, and the reply covers Incoterm, lead time, and documentation. Cutting and condition questions can ride on the same inquiry for engineering review.